Find the most up-to-date version of JASO M at Engineering JASO M Metal pipes for automobile tubing w. WALL A. 2. Classification. Type of pipe. The pipes shall be classified into the following 4 groups. 1. Jaso M Bhg2 *mm Zn Coated Double Wall Steel Tube Bundy Tube For Brake Pipe Line Of Automobile, Find Complete Details about Jaso M

Author: Moogujind Arashigami
Country: Bermuda
Language: English (Spanish)
Genre: Technology
Published (Last): 6 November 2009
Pages: 454
PDF File Size: 1.84 Mb
ePub File Size: 20.90 Mb
ISBN: 397-7-28612-273-7
Downloads: 21679
Price: Free* [*Free Regsitration Required]
Uploader: Meztigami

JASO M101 Brake Tube ASTM A-254-91, A-512-91A

Standards automobile tubingJASOmetal pipestube standard. The welded low carbon steel pipes shall be made by copper coating both surfaces or inner surface of SPCC specified in JIS Gshaping them into a jasl form, and sealing the edges by electric resistance welding, however inside surface, may not be copper coated if mutually agreed upon by the purchaser and the manufacturer.

Inspection shall be conducted by the above 6 and the results shall meet requirements naso in the above 3. Pursuant to JIS H Guarantee pressure test Examine if any leak of other defects occurred or not when pipe is applied with specified hydraulic pressure and held jaxo 5 minutes.

  LA CONSAGRACION DE LA PRIMAVERA PDF

The brazed double wall low carbon steel pipes shall be made by copper-coating both surfaces of SPCC specified in JIS G, shaping them into the form of double wall tubing, and sealing the seams by copper brazing and fusion in a reduction furnace.

Flattening Test 1 Length of test specimen shall be mm.

JASO M Brake Tube ASTM A, AA, Application:Universal

Copper and copper alloy seamless pipes and tubes C or C Tubing mainly for air brakes 2. The test shall be conducted pursuant to corrosion test specified in Table 10 and shall meet requirements in Table 6. The applicable standards for this standards are shown below. Iron rust red rust shall appear 5 spots or less per 50 cm 2 in 24 hours.

Performance of organic film shall be pursuant to Table 6 and shall meet requirements in Table 7, after the tests pursuant to Table 10 are conducted as occasion demands. The pipes shall be tested pursuant to Table 10 and shall resist the guarantee pressure specified in Table 8 without leaving injurious deformation. Method of manufacturing 4.

  APPLIED LINEAR ALGEBRA PETER J.OLVER PDF

JASO M Metal Pipes for Automobile Tubing

When the plates are pressed, the weld of tube shall be placed at 90 degrees to the direction of applied force. Examine if any leak of other defects occurred or not when pipe is applied with specified hydraulic pressure and held for 5 minutes.

Inspection shall be conducted pursuant to the above ,101 and the results shall meet requirements specified in the above 4.

Wall of the tubing shall be free from kaso or cracks after the tests pursuant to Table 10 are conducted. Designation of products shall be pursuant to the standard number, type of tubing, and type and nominal diameter of outside surface. Example if any flaws, cracks, or other defects occurred or not when the pipe was bent degrees around a cylinder having the radius as specified below.